Product parameter
It has copper as the main trace element with high strength and can be strengthened by heat treatment. The strength is only second to 7 series. It's usually used in structural materials, but also can be forged. It could be used for structural parts of aircraft, structure parts of building and transportation tools, mould, mechanical parts requiring high strength, cabinet shell etc.
Chemical composition ,Standard (max), W% | Al: balance | |||||
Si | Fe | Cu | Mn | Mg | Zn | Other |
0.5 | 0-0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.3 | Ti 0.15/Cr0.1 |
Mechanical Property (Standard Value) | T4(10mm) | H112 |
Tensile Strength(MPa) | ≥425 | 220-228 |
Yield Strength(MPa) | ≥275 | 147-150 |
Elongation(%) | ≥14 | 18-20 |
The above values is sbjuect to be different due to the different thickness.
2A12 aluminum plate is widely used in the aerospace field，Military Field，Transportation Industry，Mechanical Equipment Manufacturing, Building Decoration.
In aerospace filed, It can be processed into various forms such as thin sheets, thick plates, and profiles to manufacture important components of aircraft, such as fuselage skins, wing ribs, and spars. These components require materials with high strength, good fatigue resistance, and light weight to ensure the performance and safety of aircraft.
The interior has been scanned and tested by various advanced instruments.
Smooth surface, high flatness.
Thickness tolerance about ±1%.
Thickness<100mm, there is a protective film covering the surface (random color).
We have more than ten cutting equipment and machines.
Thickness<8mm, we sale whole plate only. The whole plate is able to be cut to smaller size.
Thickness not less than 8mm, we sale the small pieces in any dimensions.
Our system ensures all the products are traceable to provide the original factory certificate.
Product parameter
It has copper as the main trace element with high strength and can be strengthened by heat treatment. The strength is only second to 7 series. It's usually used in structural materials, but also can be forged. It could be used for structural parts of aircraft, structure parts of building and transportation tools, mould, mechanical parts requiring high strength, cabinet shell etc.
Chemical composition ,Standard (max), W% | Al: balance | |||||
Si | Fe | Cu | Mn | Mg | Zn | Other |
0.5 | 0-0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.3 | Ti 0.15/Cr0.1 |
Mechanical Property (Standard Value) | T4(10mm) | H112 |
Tensile Strength(MPa) | ≥425 | 220-228 |
Yield Strength(MPa) | ≥275 | 147-150 |
Elongation(%) | ≥14 | 18-20 |
The above values is sbjuect to be different due to the different thickness.
2A12 aluminum plate is widely used in the aerospace field，Military Field，Transportation Industry，Mechanical Equipment Manufacturing, Building Decoration.
In aerospace filed, It can be processed into various forms such as thin sheets, thick plates, and profiles to manufacture important components of aircraft, such as fuselage skins, wing ribs, and spars. These components require materials with high strength, good fatigue resistance, and light weight to ensure the performance and safety of aircraft.
The interior has been scanned and tested by various advanced instruments.
Smooth surface, high flatness.
Thickness tolerance about ±1%.
Thickness<100mm, there is a protective film covering the surface (random color).
We have more than ten cutting equipment and machines.
Thickness<8mm, we sale whole plate only. The whole plate is able to be cut to smaller size.
Thickness not less than 8mm, we sale the small pieces in any dimensions.
Our system ensures all the products are traceable to provide the original factory certificate.